The amount of flash is set by melt volume; its direction is set by geometry. The parting line, the step and the flash trap fix the appearance question on the drawing.
If the halves are misaligned the joint runs wide on one side and tight on the other. Locating features should touch before the weld faces, and should absorb assembly variation rather than locating, carrying load and fusing all at once.
A grade designation is only a name. Molecular weight, filler distribution, pigment, mould release and regrind can all move between batches, and ultrasonic welding is more sensitive to that than moulding is.
More interference is not better and less clearance is not better. What decides the value is whether the tool can hold it consistently and how the fixture supports the part.
Strength comes from the area that actually fuses, not from how long the joint looks. Corners, interrupted sections and fibre-occupied regions do not count, and getting it wrong throws off the power selection too.
Углеродное волокно твёрже стеклянного и агрессивнее к рабочей поверхности. Причина сложности сварки та же, что у стекловолокна, но ресурс сонотрода, электропроводность и пыль — это уже специфика углерода.
Антипирен не участвует в сплавлении, а его доля немала, поэтому он равносилен барьерному слою на границе раздела. Потолок задаёт материал, поэтому проектируйте под то, что огнестойкая марка действительно даёт.
PLA и подобные компостируемые смолы свариваются, но они хрупки, имеют узкий интервал плавления и различаются от партии к партии. Настоящая ловушка не в сварке, а в том, что после неё деталь всё равно должна отвечать требованию по разложению.
ПВХ легко плавится; проблема в том, что при перегреве он разлагается, а продукты разложения разъедают сонотроды и оснастку. Контроль энергии, короткие циклы и уборка по графику здесь важнее, чем повышение параметров.